Shrunken leather - leather shrinkage

Shrinkage of leather caused by heat

Leather can shrink and harden by excessive heat. Typical is damaged car leather at the top along the rear bench, the headrests and on dashboards. Leather also hardens because it dries out with time (without leather care). The leather fibers stiffen and become brittle.

This process is accelerated by the fact that the collagen of the fibers then denatures with release of the water previously bound in them. Initially, small singulated thickenings are formed in the leather fibre struccture, which subsequently expand and solidify. The density of the leather increases, but its dimensions decrease. This hardening is extremely stable. Once shrunken leather is therefore irreparably damaged and can sometiems be softened a little with appropriate care products, but the loss of surface is permanent and can not be recovered.

For wet leathers, even little heat is sufficient to shrink it. Wet leather should never be allowed to dry in the sun or on a heater. The best temperature to dry leather is normal room temperature.

Video about the shrinkage of leather.

Welle oiled and greased leather will never shrink as quickly as poorly maintained leather. The tanning methode of the leather directly influences its shrinkability. Traditionally vegetable-tanned leather already begin to shrink at 70 degrees Celsius. This looks like a high temperature, but which is reached quickly, when a convertible with wet, dark leather seats is put into the sun for drying. The leather is then "cooked" and shrinks. Modern tanning processes, such as chrome tanning, raise the threshold of leather shrinkage so that such leather starts shrinking between 85 to 110 degrees Celsius.

Condition/tanning methode	Shrinkage temperature
Rawhide	60°C - 65°C (140 - 149 °F)
After pickling before tanning	40°C - 60°C (104 - 140 °F)
Vegetable-tanned leather	70°C - 80°C (158 - 176 °F)
Chrome tanned	85°C - 100°C (185 - 212 °F)
Synthetic tanned	75°C - 85°C (167 - 185 °F)
Chamois leather	60°C - 70°C (104 - 158 °F)

Chrome tanned leather shrinks later than chrome-free leather, but then significantly stronger. Synthetic tanned leather starts shrinking at 75 degrees Celsius, but will not contract as strongly as chrome leather.

A problem of chrome-free (FOC) synthetic tanned leather is the sensitivity to moisture in the leather plus heat. Approx. 50% of all car leather is FOC. If a convertible comes into rain, a liquid runs out or a wet towel or a wet swim suit remains too long on the leather, moisture migrates through the finish, the seam holes or the perforation holes. If sun shines on such moistered leather, the matrix water (chemically bound in leather) starts boiling and the leather hardens and shrinks.

Shrinkage of synthetic tanned car leather due to moisture in leather and the heat of the sun.

The moisture of leather has an effect on the shrinkage temperature. Dry leather is more stable than wet leather. Since leather absorbs the surrounding air humidity, the parameter "moisture" must be considered in case of critical applications of leather.

Rear upholstery, above area of a classic car. - Shrunken dashboard leather of the Peugeot 307CC.

Shrunken Headrest by sun. - Fire hole in leather furniture by fallen lamp.

Even during the tanning process, the temperature to which the leather is exposed must be constantly checked. Rawhide should not be exposed to more than 30 degrees Celsius, since its stability against temperature influences is still low. During the tanning process, a temperature range from 50 to 70 degrees Celsius is generally kept. Furthermore, the temperature is to be monitored during drying, finish and embossing of the leather.

The rear upholstery top of the BMW E30 convertible is particularly prone to heat damages.

Unexplained shrinkage of individual fields on the back seat of a volvo. - Left picture: Only rear surface seat. - Right picture: Cracked leather in the back upholstery.

Left: halogen lamp. - Right: Expired hot liquid. Pulling of folds to the shrunken area is typical.

In case of cloth, the house would have burnt. Heat damage in the leather cause by a lamp.

Dashboard leather - Pre-Shrunk Leather

Automotive manufacturers and their suppliers are taking advantage of the shrinking behavior of leather to trim dashboards. In order to achieve shape stability and to ensure that the leather remains stable even under the practical conditions in the car (sunshine and possibly high humidity), the leather is sometimes "pre-shrunken". This so-called "heat setting" is carried out by exposing the leather to short-term temperatures of more than 100 degrees Celsius. Long enough to achieve a lasting shape, but also short enough to prevent the leather becoming unusable.

Dashboard completely covered with leather.

The used adhesive also plays an important role. The adhesive must be stronger than the forces of shrinkage of the leather. This can prevent shrinkage damages.

Shrunken dashboard leathers of the Peugeot 307CC.

Shrinkage of leather in the tannery

Since leather is sold by surface, the tanner tries to get an as large as possible hide by the tanning process. However, leathers are sometimes deliberately shrunken, so that the leather becomes thicker and the grain pattern is reenforced. Such treatments are known in the case of cow neck leather and sheep leather. The company www.brocantique.de is a specialist for vegetal tanned sheep leather shrinkage. When shrinking sheep leather, it loses up to 20% of the surface and becomes thicker.